高级搜索

PTFE/TiO2复合膜光催化降解水中罗丹明B研究

,  ,  ,  ,  , 

downloadPDF

上一篇

下一篇

孟琪, 程士, 周茜, 杜琦, 李华瑞, 程修文. PTFE/TiO2复合膜光催化降解水中罗丹明B研究[J]. 环境保护科学, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
引用本文: 孟琪, 程士, 周茜, 杜琦, 李华瑞, 程修文. PTFE/TiO2复合膜光催化降解水中罗丹明B研究[J]. 环境保护科学, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
shu
Meng Qi, Cheng Shi, Zhou Xi, Du Qi, Li Huarui, Cheng Xiuwen. Photocatalytic Degradation of Rhodamine B in Aquatic Solution by PTFE/TiO2 Composite Film[J]. Environmental Protection Science, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
Citation: Meng Qi, Cheng Shi, Zhou Xi, Du Qi, Li Huarui, Cheng Xiuwen. Photocatalytic Degradation of Rhodamine B in Aquatic Solution by PTFE/TiO2 Composite Film[J]. Environmental Protection Science, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
shu

PTFE/TiO2复合膜光催化降解水中罗丹明B研究

  • 1. 兰州大学资源环境学院, 甘肃 兰州 730000;

  • 2. 甘肃省环境污染预警与控制重点实验室, 甘肃 兰州 730000;

  • 3. 西部环境教育部重点实验室, 甘肃 兰州 730000

    • 作者简介: 孟琪(1995-),女,本科生。研究方向:水处理环境功能材料研制及应用。E-mail:mengq13@lzu.edu.cn
    通讯作者: 程修文, E-mail: 博士、副教授。chengxw@lzu.edu.cn
  • 基金项目:

    秦惠君与李政道中国大学生见习进修基金

    兰州大学中央高校基本科研业务费专项资金支持项目(lzujbky-2015-137)

    甘肃省自然科学基金(1506RJZA216)

    国家自然科学基金青年基金项目(51508254)基金资助

  • 中图分类号: X703

Photocatalytic Degradation of Rhodamine B in Aquatic Solution by PTFE/TiO2 Composite Film

  • 1. College of Earth Environmental Sciences, Lanzhou University, Lanzhou 730000, China;

  • 2. Key Laboratory of Environmental Pollution Prediction and Control of Gansu Province, Lanzhou 730000, China;

  • 3. Key Laboratory of Western China's Environmental Systems(Ministry of Education), Lanzhou 730000, China

    • Corresponding author: Cheng Xiuwen, 博士、副教授。chengxw@lzu.edu.cn
  • Fund Project:

  • 摘要: 以P25 TiO2为催化剂、聚四氟乙烯乳液(PTFE)为粘结剂,采用辊压法制备了PTFE/TiO2复合膜催化剂,并对其进行了SEM和XRD表征。结果表明:TiO2与PTFE乳液的质量比为4:1时其表面最为平整且分布着均匀的空隙。此外,PTFE的引入并没有改变TiO2的晶相结构与衍射峰强度。另外,随着光照时间的延长,PTFE/TiO2复合膜催化表面·OH自由基产生量呈线性增加,且RhB分子在553 nm处特征吸收峰强度逐渐降低。经过150 min光照后,RhB的光催化降解率达到87%。连续重复使用14次之后,PTFE/TiO2复合催化膜的光催化效率仅下降2%左右,这表明其可能在废水深度处理领域得到实用化应用。
    Abstract: In this study, PTFE/TiO2 composite film was fabricated through rolling process by use of P25 TiO2 as catalyst and PTFE latex as binder. The resulting samples were then characterized by SEM and XRD techniques. The results showed that the optimized quality ratio of TiO2 to PTFE latex was 4:1, in which the PTFE/TiO2 composite film possessed most smooth surface and uniform pore structure. Addition of PTFE latex didn't change the crystalline phase structure and diffraction peak intensity of TiO2. Moreover, with the extension of light irradiation, the yield amount of·OH at PTFE/TiO2 composite film/water interface increased linearly and the characteristic adsorption peak intensity of RhB at 553 nm decreased gradually. Within 150 min of illumination, photocatalytic efficiency of RhB reached to 87%. After 14 times of continuous reuse, the photocatalytic efficiency only declined by 2%, indicating that such PTFE/TiO2 composite film could be practically applied in the field of advanced wastewater treatment.
  • 加载中
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  687
  • HTML全文浏览数:  687
  • PDF下载数:  5
  • 施引文献:  0
出版历程
  • 收稿日期:  2016-01-20
孟琪, 程士, 周茜, 杜琦, 李华瑞, 程修文. PTFE/TiO2复合膜光催化降解水中罗丹明B研究[J]. 环境保护科学, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
引用本文: 孟琪, 程士, 周茜, 杜琦, 李华瑞, 程修文. PTFE/TiO2复合膜光催化降解水中罗丹明B研究[J]. 环境保护科学, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
shu
Meng Qi, Cheng Shi, Zhou Xi, Du Qi, Li Huarui, Cheng Xiuwen. Photocatalytic Degradation of Rhodamine B in Aquatic Solution by PTFE/TiO2 Composite Film[J]. Environmental Protection Science, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
Citation: Meng Qi, Cheng Shi, Zhou Xi, Du Qi, Li Huarui, Cheng Xiuwen. Photocatalytic Degradation of Rhodamine B in Aquatic Solution by PTFE/TiO2 Composite Film[J]. Environmental Protection Science, 2016, (3): 79-81,108. doi: 10.16803/j.cnki.issn.1004-6216.2016.03.015
shu

PTFE/TiO2复合膜光催化降解水中罗丹明B研究

    通讯作者: 程修文, E-mail: 博士、副教授。chengxw@lzu.edu.cn
    作者简介: 孟琪(1995-),女,本科生。研究方向:水处理环境功能材料研制及应用。E-mail:mengq13@lzu.edu.cn
  • 1. 兰州大学资源环境学院, 甘肃 兰州 730000;
  • 2. 甘肃省环境污染预警与控制重点实验室, 甘肃 兰州 730000;
  • 3. 西部环境教育部重点实验室, 甘肃 兰州 730000
  • 收稿日期:  2016-01-20
基金项目:

秦惠君与李政道中国大学生见习进修基金

兰州大学中央高校基本科研业务费专项资金支持项目(lzujbky-2015-137)

甘肃省自然科学基金(1506RJZA216)

国家自然科学基金青年基金项目(51508254)基金资助

摘要: 以P25 TiO2为催化剂、聚四氟乙烯乳液(PTFE)为粘结剂,采用辊压法制备了PTFE/TiO2复合膜催化剂,并对其进行了SEM和XRD表征。结果表明:TiO2与PTFE乳液的质量比为4:1时其表面最为平整且分布着均匀的空隙。此外,PTFE的引入并没有改变TiO2的晶相结构与衍射峰强度。另外,随着光照时间的延长,PTFE/TiO2复合膜催化表面·OH自由基产生量呈线性增加,且RhB分子在553 nm处特征吸收峰强度逐渐降低。经过150 min光照后,RhB的光催化降解率达到87%。连续重复使用14次之后,PTFE/TiO2复合催化膜的光催化效率仅下降2%左右,这表明其可能在废水深度处理领域得到实用化应用。