高级搜索

烟气脱硫过程锰催化氧化亚硫酸钙的研究

,  ,  ,  , 

downloadPDF

上一篇

下一篇

杨剑, 文娟, 董凌燕, 刘清才, 杜云贵. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报, 2007, 1(9): 109-112.
引用本文: 杨剑, 文娟, 董凌燕, 刘清才, 杜云贵. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报, 2007, 1(9): 109-112.
shu
Yang Jian, Wen Juan, Dong Lingyan, Liu Qingcai, Du Yungui. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering, 2007, 1(9): 109-112.
Citation: Yang Jian, Wen Juan, Dong Lingyan, Liu Qingcai, Du Yungui. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering, 2007, 1(9): 109-112.
shu

烟气脱硫过程锰催化氧化亚硫酸钙的研究

  • 1.

    重庆大学材料科学与工程学院，重庆 400044；2.中电投远达环保工程有限公司，重庆 400060

  • 2.

    中电投远达环保工程有限公司，重庆 400060

  • 基金项目:

  • 中图分类号: X701.3

Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate

  • 1.

    College of Materials Science and Engineering, Chongqing University, Chongqing 400044；2. CPI Yuanda Environmental Protection Engineering Co. Ltd., Chongqing 400060

  • 2.

    CPI Yuanda Environmental Protection Engineering Co. Ltd., Chongqing 400064

  • Fund Project:

  • 摘要: 利用直径280 mm、高320 mm的间歇式搅拌槽，在MnSO4加入浓度为0～0.05 mol/L的情况下，对亚硫酸钙悬浮液进行了催化氧化实验研究。实验结果表明，锰离子的加入会改变亚硫酸钙的氧化机理及氧化过程，表现为终点氧化率和氧化速率的变化。当Mn2+浓度为0.05 mol/L时，亚硫酸钙的终点氧化率比未加入Mn2+时高30%；此外，与非催化反应过程相比，Mn2+的加入能使亚硫酸钙在一个更宽的浓度范围内(0.02～0.073 mol/L)和一个更宽的时间范围内(20～100 min)均保持较高的氧化速率水平。
    Abstract: The influence of manganese ion on oxidation of calcium sulfite has been researched in a batch agitated tank which diameter was 280 mm and height was 320 mm. The concentration of manganese ion added was between 0 to 0.05 mol/L.The experimental results indicated that the addition of manganese ion could change the mechanism and the process of oxidation, which represented the changes of oxidation rate and oxidation ratio of calcium sulfite. When manganese ion concentration was 0.05 mol/L, the oxidation rate of calcium sulfite was 30% higher than that of none manganese ion. Besides, the existence of manganese ion could keep the oxidation rate of calcium sulfite on a high level in wider ranges of time(20~100 min) and calcium sulfite concentration(0.02~0.073 mol/L).
  • 加载中
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  2272
  • HTML全文浏览数:  1227
  • PDF下载数:  1312
  • 施引文献:  0
出版历程
  • 收稿日期:  2007-07-16
杨剑, 文娟, 董凌燕, 刘清才, 杜云贵. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报, 2007, 1(9): 109-112.
引用本文: 杨剑, 文娟, 董凌燕, 刘清才, 杜云贵. 烟气脱硫过程锰催化氧化亚硫酸钙的研究[J]. 环境工程学报, 2007, 1(9): 109-112.
shu
Yang Jian, Wen Juan, Dong Lingyan, Liu Qingcai, Du Yungui. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering, 2007, 1(9): 109-112.
Citation: Yang Jian, Wen Juan, Dong Lingyan, Liu Qingcai, Du Yungui. Study on catalytic oxidation of calcium sulfite in flue gas desulfurization process by using manganese sulfate[J]. Chinese Journal of Environmental Engineering, 2007, 1(9): 109-112.
shu

烟气脱硫过程锰催化氧化亚硫酸钙的研究

  • 1. 重庆大学材料科学与工程学院，重庆 400044；2.中电投远达环保工程有限公司，重庆 400060
  • 2. 中电投远达环保工程有限公司，重庆 400060
  • 收稿日期:  2007-07-16
基金项目:

摘要: 利用直径280 mm、高320 mm的间歇式搅拌槽，在MnSO4加入浓度为0～0.05 mol/L的情况下，对亚硫酸钙悬浮液进行了催化氧化实验研究。实验结果表明，锰离子的加入会改变亚硫酸钙的氧化机理及氧化过程，表现为终点氧化率和氧化速率的变化。当Mn2+浓度为0.05 mol/L时，亚硫酸钙的终点氧化率比未加入Mn2+时高30%；此外，与非催化反应过程相比，Mn2+的加入能使亚硫酸钙在一个更宽的浓度范围内(0.02～0.073 mol/L)和一个更宽的时间范围内(20～100 min)均保持较高的氧化速率水平。